- 密度 [g/cm3]: 2.0
- 吸水率 [%]: 0.25
- 缺口冲击强度: 0.32
- 弯曲强度 [MPa]: 83.0
- 弯曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 g/cc | 0.0723 lb/in³ | |
| Apparent Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | |
| Water Absorption | 0.25 % | 0.25 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 65 | 65 | |
| Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | |
| Flexural Strength | 103 MPa | 14900 psi | |
| Flexural Modulus | 14.0 GPa | 2030 ksi | |
| Compressive Strength | 193 MPa | 28000 psi | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | |
| Dielectric Constant | 4.2 @Frequency 1000 Hz | 4.2 @Frequency 1000 Hz | Wet |
| 4.5 @Frequency 1e+6 Hz | 4.5 @Frequency 1e+6 Hz | Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.011 @Frequency 1e+6 Hz | 0.011 @Frequency 1e+6 Hz | Wet |
| 0.012 @Frequency 1000 Hz | 0.012 @Frequency 1000 Hz | Wet | |
| Arc Resistance | 180 sec | 180 sec | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 25.0 µm/m-°C @Temperature 20.0 °C | 13.9 µin/in-°F @Temperature 68.0 °F | Alpha 1 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | Alpha 2 |
| Thermal Conductivity | 1.2561 W/m-K | 8.7173 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | |
| Glass Transition Temp, Tg | 165 °C | 329 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 175 °C | 302 - 347 °F | Molding temperature |