| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | |||
| Viscosity | 25000 cP | 25000 cP | Mixed Viscosity | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 75 | 75 | |||
| Flexural Strength | 70.3 MPa | 10200 psi | ASTM D790 | ||
| Shear Strength | 20.7 MPa | 3000 psi | ASTM D1002-94 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.20e+14 ohm-cm | 1.20e+14 ohm-cm | |||
| Dielectric Constant | 3.12 @Frequency 1000 Hz | 3.12 @Frequency 1000 Hz | |||
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | |||
| Dissipation Factor | 0.010 | 0.010 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 48.6 µm/m-°C @Temperature 20.0 °C | 27.0 µin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -65.0 °C | -85.0 °F | |||
| Shrinkage | 0.20 % | 0.20 % | Cure Shrinkage | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min | 2.00 hour | at 200°F (Recommended Cure) | ||
| 1440 - 2880 min | 24.0 - 48.0 hour | Room Temperature (Alternate Cure) | |||
| Pot Life | 240 min | 240 min | 100 gm mass @ 25°C | ||
| Descriptive Properties | |||||
| Chemical Resistance | Good | ||||
| Mix Ratio by Weight | 1:1 | resin:hardener | |||