- 密度 [g/cm3]: 2.2
- 吸水率 [%]: 0.12
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.20 g/cc | 0.0795 lb/in³ | ASTM D792 Method A | ||
| Water Absorption | 0.12 % | 0.12 % | IPC TM-650 2.6.2.1 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 60.0 MPa | 8700 psi | IPC TM-650 2.4.18.3 | ||
| Flexural Strength | 180 MPa | 26100 psi | IPC TM-650 2.4.4 | ||
| Peel Strength | 0.841 kN/m | 4.80 pli | To Copper (1 oz./35 micron); After Process Solutions; IPC TM-650 2.4.8 | ||
| 0.877 kN/m | 5.00 pli | To Copper (1 oz./35 micron); After Thermal Stress; IPC TM-650 2.4.8 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.20e+15 ohm-cm | 1.20e+15 ohm-cm | C96/35/90; IPC TM-650 2.5.17.1 | ||
| 1.50e+15 ohm-cm | 1.50e+15 ohm-cm | E24/125; IPC TM-650 2.5.17.1 | |||
| Surface Resistance | 2.80e+14 ohm | 2.80e+14 ohm | C96/35/90; IPC TM-650 2.5.17.1 | ||
| 4.40e+14 ohm | 4.40e+14 ohm | E24/125; IPC TM-650 2.5.17.1 | |||
| Dielectric Constant | 4.9 @Frequency 1.00e+9 Hz | 4.9 @Frequency 1.00e+9 Hz | IPC TM-650 2.5.5.9 | ||
| 5.2 @Frequency 1.00e+6 Hz | 5.2 @Frequency 1.00e+6 Hz | IPC TM-650 2.5.5.3 | |||
| Dielectric Strength | >= 39.4 kV/mm | >= 1000 kV/in | IPC TM-650 2.5.6.2 | ||
| Dielectric Breakdown | >= 50000 V | >= 50000 V | IPC TM-650 2.5.6 | ||
| Dissipation Factor | 0.013 @Frequency 1.00e+6 Hz | 0.013 @Frequency 1.00e+6 Hz | IPC TM-650 2.5.5.3 | ||
| Arc Resistance | >= 150 sec | >= 150 sec | IPC TM-650 2.5.1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 19.0 - 20.0 µm/m-°C | 10.6 - 11.1 µin/in-°F | x ,y direction; IPC TM-650 2.4.41 | ||
| CTE, linear, Transverse to Flow | 22.0 µm/m-°C @Temperature <=180 °C | 12.2 µin/in-°F @Temperature <=356 °F | z (< Tg); IPC TM-650 2.4.24 | ||
| 175 µm/m-°C @Temperature >=180 °C | 97.2 µin/in-°F @Temperature >=356 °F | z (> Tg); IPC TM-650 2.4.24 | |||
| Thermal Conductivity | 2.00 W/m-K | 13.9 BTU-in/hr-ft²-°F | Z-axis; ASTM E1461 | ||
| 3.50 W/m-K | 24.3 BTU-in/hr-ft²-°F | X/Y-axis; ASTM E1461 | |||
| Glass Transition Temp, Tg | 170 °C | 338 °F | DSC; IPC TM-650 2.4.25 | ||
| 180 °C | 356 °F | TMA; IPC TM-650 2.4.24 | |||
| Decomposition Temperature | 340 °C | 644 °F | Onset; IPC TM-650 2.3.41 | ||
| 400 °C | 752 °F | 5 percent; IPC TM-650 2.3.41 | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Descriptive Properties | |||||
| Dielectric Withstand Voltage (VDC) | > 5000 | HiPot; IPC TM-650 2.5.7.2 | |||
| IPC Delamination - T260 (minutes) | > 60 | IPC TM-650 2.4.24.1 | |||
| IPC Delamination - T288 (minutes) | > 15 | IPC TM-650 2.4.24.1 | |||
| IPC Delamination - T300 (minutes) | > 5 | IPC TM-650 2.4.24.1 | |||
| Z-Axis Expansion (%) | 1.8 | IPC TM-650 2.4.24 (50-260°C) | |||