- 弯曲强度 [MPa]: 31.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore D | 89 | 89 | |||
| Tensile Strength, Ultimate | 31.0 MPa | 4500 psi | after optimum cure | ||
| Elongation at Break | 2.7 % | 2.7 % | |||
| Adhesive Bond Strength | 41.0 MPa | 5950 psi | Steel-Steel; after optimum cure | ||
| 12.8 MPa @Temperature 25.0 °C | 1850 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| 13.4 MPa @Temperature 82.2 °C | 1950 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 13.4 MPa @Temperature -54.4 °C | 1950 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C | 10.0 µin/in-°F @Temperature 68.0 °F | |||
| Glass Transition Temp, Tg | 92.0 °C | 198 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 93.3 °C | 200 °F | Optimum cure is 1 hr. @ 200°F | ||
| Pot Life | 4320 min | 4320 min | Max working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Grey | ||||
| Mix Ratio | 40/1 | By Weight | |||