- 密度 [g/cm3]: 1.92
- 缺口冲击强度: 0.25
- 弯曲强度 [MPa]: 103.0
- 弯曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.92 g/cc | 0.0694 lb/in³ | |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | |
| Spiral Flow | 64.0 - 90.0 cm | 25.2 - 35.4 in | 177°C/1000 psi |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 78 | 78 | |
| Tensile Strength, Ultimate | 103 MPa | 14900 psi | |
| Tensile Modulus | 16.0 GPa | 2320 ksi | |
| Flexural Strength | 145 MPa | 21000 psi | |
| Flexural Modulus | 17.0 GPa | 2470 ksi | |
| Izod Impact, Notched | 0.250 J/cm | 0.468 ft-lb/in | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.08 @Frequency 1000 Hz | 4.08 @Frequency 1000 Hz | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | |
| Dissipation Factor | 0.0040 @Frequency 1000 Hz | 0.0040 @Frequency 1000 Hz | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 27.0 µm/m-°C @Temperature 20.0 °C | 15.0 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature 20.0 °C | 45.0 µin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 1.00 W/m-K | 6.94 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | |
| Glass Transition Temp, Tg | 150 - 160 °C | 302 - 320 °F | |
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 171 - 193 °C | 340 - 379 °F | Molding temperature |