- 密度 [g/cm3]: 0.49
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.490 g/cc | 0.0177 lb/in³ | ASTM D1475 | ||
| Water Absorption | <= 0.40 % | <= 0.40 % | ASTM D570 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 53 | 53 | Cured; ASTM D2240 | ||
| Compressive Yield Strength | 14.87 MPa | 2156 psi | ASTM D695 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 - 180 min | 2.00 - 3.00 hour | 2 to 3 hours to shape at 77°F. | ||
| 300 - 360 min | 5.00 - 6.00 hour | 5 to 6 hours to send at 77°F. | |||
| 1440 min | 24.0 hour | 24 hours to full cure at 77°F. | |||
| Pot Life | 25 - 30 min | 25 - 30 min | ASTM D2471 | ||
| Gel Time | 25.0 - 30.0 min | 25.0 - 30.0 min | Value for 4 fl. oz.; ASTM D2471 | ||
| Descriptive Properties | |||||
| Color | Light Grayish-tan | ||||
| Mix Ratio | 100:50 | Resin:Hardener by Weight | |||
| 2:1 | Resin:Hardener by Volume | ||||