- 密度 [g/cm3]: 1.78
- 缺口冲击强度: 6.41
- 弯曲强度 [MPa]: 65.5
- 弯曲模量 [MPa]: 8.27
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.10 % | <= 0.10 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | Cold Part VS Cold Tool; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 55 | 55 | ASTM D2583 |
| Hardness, Rockwell M | 111 | 111 | ASTM D785 |
| Tensile Strength, Ultimate | 65.5 MPa | 9500 psi | ASTM D638 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ASTM D638 |
| Flexural Strength | 159 MPa | 23000 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | Tangent; ASTM D790 |
| Compressive Strength | 145 MPa | 21000 psi | ASTM D695 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 0.30 | 0.30 | % Loss 1000 Cycles; FTMS1091 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Flexural Load; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/4 in; UL746 |
| V-0 | V-0 | 1/8 in; UL746 | |
| V-0 | V-0 | 1/16 in; UL746 | |