- 密度 [g/cm3]: 1.9
- 吸水率 [%]: 0.05
- 缺口冲击强度: 12.8
- 断裂伸长率 [%]: 427
- 弯曲强度 [MPa]: 261.0
- 弯曲模量 [MPa]: 17.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 261 MPa | 37900 psi | ASTM D638 |
| Tensile Modulus | 26.8 GPa | 3890 ksi | ASTM D638 |
| Flexural Yield Strength | 427 MPa | 61900 psi | ASTM D790 |
| 365 MPa @Temperature 115 °C | 52900 psi @Temperature 239 °F | ASTM D790 | |
| Flexural Modulus | 17.9 GPa | 2600 ksi | ASTM D790 |
| 16.2 GPa @Temperature 115 °C | 2350 ksi @Temperature 239 °F | ASTM D790 | |
| Compressive Yield Strength | 248 MPa | 36000 psi | ASTM D695 |
| Compressive Modulus | 0.0172 GPa | 2.49 ksi | ASTM D695 |
| Izod Impact, Notched | 12.8 J/cm | 24.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 300 °C | 572 °F | Short Term |
| Glass Transition Temp, Tg | 160 °C | 320 °F | DMA, ASTM D4065 |
| Shrinkage | 0.0010 % | 0.0010 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 132 - 149 °C | 270 - 300 °F | Mold temperature |
| Shelf Life | 2.00 Month @Temperature 23.9 °C | 2.00 Month @Temperature 75.0 °F | |