- 密度 [g/cm3]: 1.9
- 吸水率 [%]: 0.35
- 缺口冲击强度: 15.0
- 断裂伸长率 [%]: 413
- 弯曲强度 [MPa]: 275.0
- 弯曲模量 [MPa]: 17.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ASTM D792 |
| Water Absorption | 0.35 % | 0.35 % | 24 Hrs. ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 65 | 65 | ASTM D2583 |
| Tensile Strength, Ultimate | 275 MPa | 39900 psi | ASTM D638 |
| Flexural Yield Strength | 413 MPa | 59900 psi | ASTM D790 |
| Flexural Modulus | 17.2 GPa | 2490 ksi | ASTM D790 |
| Izod Impact, Notched | 15.0 J/cm | 28.1 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 5.00e+14 ohm-cm | 5.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 3.00e+14 ohm | 3.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 4.7 | 4.7 | ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | ASTM D149 |
| Dissipation Factor | 0.0090 | 0.0090 | ASTM D150 |
| Arc Resistance | 134 sec | 134 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-0 @Thickness 2.50 mm | V-0 @Thickness 0.0984 in | |
| Shrinkage | 0.0010 % | 0.0010 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 132 - 149 °C | 270 - 300 °F | Mold temperature |