- 密度 [g/cm3]: 1.83
- 吸水率 [%]: 0.2
- 缺口冲击强度: 4.8
- 弯曲强度 [MPa]: 58.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.83 g/cc | 0.0661 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 58.0 MPa | 8410 psi | ASTM D638 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ASTM D638 |
| Flexural Strength | 170 MPa | 24700 psi | ASTM D790 |
| Compressive Strength | 215 MPa | 31200 psi | ASTM D695 |
| Shear Strength | 83.0 MPa | 12000 psi | ASTM D732 |
| Izod Impact, Notched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 8.23e+14 ohm | 8.23e+14 ohm | Insulation Resistance, ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | ASTM D150 |
| 4.2 @Frequency 60 Hz | 4.2 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | Perpendicular, Short-term, in air; ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz | 0.010 @Frequency 1e+6 Hz | ASTM D150 |
| 0.011 @Frequency 60 Hz | 0.011 @Frequency 60 Hz | ASTM D150 | |
| Arc Resistance | 181 sec | 181 sec | ASTM D495 |
| Comparative Tracking Index | >= 500 V | >= 500 V | UL746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL746A |
| High Amp Arc Ignition, HAI | 200 arcs | 200 arcs | UL746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 mm/min | 0.000 in/min | UL746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | ASTM C177 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | NEMA temperature |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical with Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 39 % | 39 % | ASTM D2862 |