- 密度 [g/cm3]: 1.84
- 吸水率 [%]: 0.2
- 缺口冲击强度: 4.3
- 弯曲强度 [MPa]: 69.0
- 弯曲模量 [MPa]: 6.90
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.84 g/cc | 0.0665 lb/in³ | ASTM D572 |
Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
Mechanical Properties | Metric | English | Comments |
Hardness, Barcol | 46 | 46 | |
Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | |
Flexural Strength | 145 MPa | 21000 psi | |
Flexural Modulus | 6.90 GPa | 1000 ksi | |
Compressive Strength | 207 MPa | 30000 psi | |
Shear Strength | 97.0 MPa | 14100 psi | ASTM D732 |
Izod Impact, Notched | 4.30 J/cm | 8.06 ft-lb/in | edgewise; ASTM D256 |
Electrical Properties | Metric | English | Comments |
Dielectric Constant | 4.4 @Frequency 60 Hz | 4.4 @Frequency 60 Hz | ASTM D150 |
Dielectric Strength | 22.0 kV/mm @Thickness 1.59 mm | 559 kV/in @Thickness 0.0625 in | Perpendicular, Short Time in Oil and Air; ASTM D149 |
Dissipation Factor | 0.031 @Frequency 60 Hz | 0.031 @Frequency 60 Hz | ASTM D150 |
Arc Resistance | 180 sec | 180 sec | ASTM D495 |
Comparative Tracking Index | >= 500 V | >= 500 V | |
Thermal Properties | Metric | English | Comments |
Maximum Service Temperature, Air | 130 °C | 266 °F | Approximate temperature class |
Flammability, UL94 | V-0 | V-0 | File No.E81893 |