- 缺口冲击强度: 7.0
- 弯曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 - 1.85 g/cc | 1.70 - 1.85 g/cc | |
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 55.0 MPa | 7980 psi | ASTM D638 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ASTM D638 |
| Flexural Strength | 135 MPa | 19600 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 3.80 GPa | 551 ksi | Calculated |
| Izod Impact, Notched | 7.00 J/cm | 13.1 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.00 J/cm | 16.9 ft-lb/in | ASTM D4812 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | ASTM D149 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 600 V | 600 V | ASTM D2303 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | Z Direction |
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | XY Direction |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746C |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746C |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746C |
| Flammability, UL94 | V-0 @Thickness 2.50 mm | V-0 @Thickness 0.0984 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 °C | 302 °F | Compression Molding |
| Clamp Pressure | 3.45 - 6.89 MPa | 500 - 1000 psi | Molding Pressure |