| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | >= 25.4 microns | >= 1.00 mil | Side 1 | ||
| >= 25.4 microns | >= 1.00 mil | Side 2 | |||
| 38.1 microns | 1.50 mil | Polyethylene Interleave | |||
| 50.8 microns | 2.00 mil | Unprimed Coated 1080 Fiberglass (same as 108/no plied yarns), Substrate | |||
| 63.5 microns | 2.50 mil | Primed Coated 1080 Fiberglass (same as 108/no plied yarns), Substrate | |||
| 114 - 165 microns | 4.50 - 6.50 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property | ||
| Tensile Strength | >= 5.52 MPa | >= 800 psi | Compound Property | ||
| Elongation at Break | >= 550 % | >= 550 % | Compound Property | ||
| Peel Strength | >= 0.701 kN/m | >= 4.00 pli | [ppi], Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| UL RTI, Electrical | 220 °C | 428 °F | per UL Card E54153 | ||
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | per UL Card E54153 | ||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 177 °C | 0.250 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 120 min @Temperature 232 °C | 2.00 hour @Temperature 450 °F | Recommended Postcure Cycle | |||
| Shelf Life | 6.00 Month @Temperature <=23.9 °C | 6.00 Month @Temperature <=75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 4.5 - 5.5 | ||||
| Uncoated Fabric Break Strength | 40 lb/in | Fill Direction, Substrate Property | |||
| 70 lb/in | Warp Direction, Substrate Property | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.