- 密度 [g/cm3]: 1.32
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 50.8 microns | 2.00 mil | Side 1; Arlon SQA-TMS-003 | ||
| 76.2 microns | 3.00 mil | Interleave | |||
| 127 microns | 5.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 381 microns | 15.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 37 | 37 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.55 MPa | 950 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 620 % | 620 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 26.3 kN/m | 150 pli | Silicone Property; ASTM D624 | ||
| Peel Strength | 2.10 kN/m | 12.0 pli | Bond Strength; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 28.3 kV/mm | 720 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| UL RTI, Electrical | 200 °C | 392 °F | E 54153 | ||
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | E 54153 | ||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Red | Substrate | ||||
| Total Product Weight (oz/yd2) | 15.6 | Arlon SQA-TMS-025 | |||