- 密度 [g/cm3]: 1.34
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Interleave | ||
| 102 microns | 4.00 mil | Layer 1; Arlon SQA-TMS-003 | |||
| 305 microns | 12.0 mil | Layer 2; Arlon SQA-TMS-003 | |||
| 457 microns | 18.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 864 microns | 34.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 37 | 37 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.55 MPa | 950 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 620 % | 620 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 26.3 kN/m | 150 pli | Silicone Property; ASTM D624 | ||
| Peel Strength | 5.47 kN/m | 31.2 pli | Bond Strength; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| UL RTI, Electrical | 200 °C | 392 °F | E54153 | ||
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | E54153 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 35.7 | Arlon SQA-TMS-025 | |||