- 密度 [g/cm3]: 1.32
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 63.5 microns | 2.50 mil | Interleave | ||
| 165 microns | 6.50 mil | Side 2; Arlon SQA-TMS-003 | |||
| 191 microns | 7.50 mil | Side 1; Arlon SQA-TMS-003 | |||
| 406 microns | 16.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 762 microns | 30.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 | 55 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 7.93 MPa | 1150 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 550 % | 550 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 21.0 kN/m | 120 pli | Silicone Property; ASTM D624 | ||
| Peel Strength | 1.53 kN/m | 8.70 pli | Bond Strength; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | V-0 | V-0 | per card E54153 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Brown | ||||
| Total Product Weight (oz/yd2) | 31.2 | Arlon SQA-TMS-025 | |||