- 密度 [g/cm3]: 1.25
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 25.4 microns | 1.00 mil | Laminated Metalized Polymer Film; Arlon SQA-TMS-003 | ||
| 38.1 microns | 1.50 mil | Side 1; Arlon SQA-TMS-003 | |||
| 63.5 microns | 2.50 mil | Side 2; Arlon SQA-TMS-003 | |||
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 330 microns | 13.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 | 50 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 5.86 MPa | 850 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 350 % | 350 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 1.05 kN/m | 6.00 pli | Bond Strength(S1 to S2); SQA-TMS-011 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | <= 3.0 | <= 3.0 | [in], Char Length; FTMS 191A; Method 5903 | ||
| <= 25 | <= 25 | [sec], Flame and Glow; FTMS 191A; Method 5903 | |||
| Shrinkage, MD | 0.30 % @Temperature 200 °C, Time 600 sec | 0.30 % @Temperature 392 °F, Time 0.167 hour | |||
| Shrinkage, TD | 0.50 % @Temperature 200 °C, Time 600 sec | 0.50 % @Temperature 392 °F, Time 0.167 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | ||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Total Product Weight (oz/yd2) | 13.9 | Arlon SQA-TMS-025 | |||