Arlon 514B12R006 0.006" Cured Silicone Rubber with Fiberglass Substrate

Arlon 514B12R006 0.006" Cured Silicone Rubber with Fiberglass Substrate 物性表: Arlon 514B12R006 0.006" Cured Silicone Rubber with Fiberglass Substrate物性表及特性介绍,Arlon 514B12R006 0.006" Cured Silicone Rubber with Fiberglass Substrate注塑参数详情,如需Arlon 514B12R006 0.006" Cured Silicone Rubber with Fiberglass Substrate下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.3
 
Physical PropertiesMetricEnglishComments
Density 1.30 g/cc0.0470 lb/in³Silicone Property; Arlon SQA-TMS-024
Thickness 50.8 microns2.00 milSide 1; Arlon SQA-TMS-003
 102 microns4.00 milSubstrate; Arlon SQA-TMS-003
 152 microns6.00 milOverall Thickness; Arlon SQA-TMS-003
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore A 6060Silicone Property; ASTM D2240
Tensile Strength 5.72 MPa830 psiSilicone Property; ASTM D412
Elongation at Break 150 %150 %Silicone Property; ASTM D412
Tear Strength 9.64 kN/m55.0 pliSilicone Property; Die B; ASTM D624
 
Electrical PropertiesMetricEnglishComments
Dielectric Strength 59.1 kV/mm1500 kV/inASTM D149
 
Thermal PropertiesMetricEnglishComments
Maximum Service Temperature, Inert 232 °C450 °F
Minimum Service Temperature, Air -56.7 °C-70.0 °F
Flammability Test 0.250.25Inches; Char Length; FAR 25.853 App F, Pt. 1, S. Aii
 1.01.0Seconds; Flame and Glow Time; FAR 25.853 App F, Pt. 1, S. Aii
 
Processing PropertiesMetricEnglishComments
Cure Time 120 min
@Temperature 204 °C
2.00 hour
@Temperature 400 °F
Recommended Post Cure Cycle
Shelf Life 60.0 Month
@Temperature 23.9 °C
60.0 Month
@Temperature 75.0 °F
 
Descriptive Properties
ColorRed
Total Product Weight (oz/yd2)5.6Arlon SQA-TMS-025

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-34432.html

免责声明: 本文 Arlon 514B12R006 0.006" Cured Silicone Rubber with Fiberglass Substrate 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4