- 密度 [g/cm3]: 0.5
- 弯曲强度 [MPa]: 7.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.500 - 1.17 g/cc | 0.0181 - 0.0423 lb/in³ | Average value: 0.965 g/cc Grade Count:26 |
| Viscosity | 1400 - 300000 cP | 1400 - 300000 cP | Average value: 129000 cP Grade Count:42 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60.0 - 70.0 | 60.0 - 70.0 | Average value: 64.4 Grade Count:8 |
| Tensile Strength, Ultimate | 7.60 - 31.0 MPa | 1100 - 4500 psi | Average value: 17.1 MPa Grade Count:30 |
| Elongation at Break | 5.00 - 1660 % | 5.00 - 1660 % | Average value: 96.6 % Grade Count:39 |
| Elongation at Yield | 15.0 - 70.0 % | 15.0 - 70.0 % | Average value: 36.3 % Grade Count:8 |
| Modulus of Elasticity | 0.0689 - 1.90 GPa | 10.0 - 275 ksi | Average value: 0.579 GPa Grade Count:25 |
| Shear Strength | 1.38 - 24.1 MPa | 200 - 3500 psi | Average value: 12.8 MPa Grade Count:25 |
| Adhesive Bond Strength | 0.600 - 29.0 MPa | 87.0 - 4200 psi | Average value: 19.5 MPa Grade Count:23 |
| Tensile Impact Strength | 35.7 - 46.2 kJ/m² | 17.0 - 22.0 ft-lb/in² | Average value: 41.3 kJ/m² Grade Count:9 |
| Peel Strength | 1.75 - 11.4 kN/m | 10.0 - 65.0 pli | Average value: 5.00 kN/m Grade Count:18 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 93.3 - 121 °C | 200 - 250 °F | Average value: 119 °C Grade Count:44 |
| Minimum Service Temperature, Air | -55.0 - -40.0 °C | -67.0 - -40.0 °F | Average value: -51.6 °C Grade Count:38 |
| Flash Point | 10.6 °C | 51.0 °F | Average value: 10.6 °C Grade Count:29 |
| Processing Properties | Metric | English | Comments |
| Cure Time | 2.00 - 240 min | 0.0333 - 4.00 hour | Average value: 52.6 min Grade Count:10 |
| Pot Life | 1.00 - 105 min | 1.00 - 105 min | Average value: 24.6 min Grade Count:25 |