- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.683
- 拉伸强度 [MPa]: 40.0
- 断裂伸长率 [%]: 60.0
- 弯曲强度 [MPa]: 41.0
- 弯曲模量 [MPa]: 7.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 - 1.45 g/cc | 0.0415 - 0.0524 lb/in³ | Average value: 1.36 g/cc Grade Count:29 |
| Water Absorption | 0.300 - 2.20 % | 0.300 - 2.20 % | Average value: 0.806 % Grade Count:10 |
| Linear Mold Shrinkage | 0.00250 - 0.00300 cm/cm | 0.00250 - 0.00300 in/in | Average value: 0.00275 cm/cm Grade Count:10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 76.0 - 105 | 76.0 - 105 | Average value: 85.8 Grade Count:4 |
| Hardness, Rockwell M | 98.0 - 112 | 98.0 - 112 | Average value: 107 Grade Count:4 |
| Ball Indentation Hardness | 130 - 170 MPa | 18900 - 24700 psi | Average value: 147 MPa Grade Count:7 |
| Tensile Strength, Ultimate | 41.0 - 58.0 MPa | 5950 - 8410 psi | Average value: 50.1 MPa Grade Count:10 |
| Tensile Strength, Yield | 40.0 - 100 MPa | 5800 - 14500 psi | Average value: 63.3 MPa Grade Count:9 |
| Modulus of Elasticity | 6.00 - 8.00 GPa | 870 - 1160 ksi | Average value: 7.14 GPa Grade Count:7 |
| Flexural Yield Strength | 60.0 - 180 MPa | 8700 - 26100 psi | Average value: 94.6 MPa Grade Count:25 |
| Flexural Modulus | 7.00 - 11.0 GPa | 1020 - 1600 ksi | Average value: 9.38 GPa Grade Count:8 |
| Compressive Yield Strength | 80.0 - 320 MPa | 11600 - 46400 psi | Average value: 146 MPa Grade Count:29 |
| Izod Impact, Notched | 0.683 - 1.44 J/cm | 1.28 - 2.71 ft-lb/in | Average value: 0.991 J/cm Grade Count:10 |
| Izod Impact, Notched (ISO) | 8.00 - 55.0 kJ/m² | 3.81 - 26.2 ft-lb/in² | Average value: 19.9 kJ/m² Grade Count:9 |
| Coefficient of Friction | 0.0200 - 0.200 | 0.0200 - 0.200 | Average value: 0.0650 Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+8 ohm | 1.00e+8 ohm | Average value: 1.00e+8 ohm Grade Count:5 |
| Insulation Resistance | 100000 - 2.00e+7 ohm | 100000 - 2.00e+7 ohm | Average value: 4.44e+6 ohm Grade Count:10 |
| Dielectric Constant | 5.00 - 10.0 | 5.00 - 10.0 | Average value: 6.00 Grade Count:6 |
| Dielectric Strength | 3.10 - 20.0 kV/mm | 78.7 - 508 kV/in | Average value: 11.0 kV/mm Grade Count:9 |
| Dielectric Breakdown | >= 1000 V @Temperature 90.0 - 90.0 °C | >= 1000 V @Temperature 194 - 194 °F | Average value: 7220 V Grade Count:9 |
| >= 1000 V @Time 20.0 - 60.0 sec | >= 1000 V @Time 0.00556 - 0.0167 hour | Average value: 7220 V Grade Count:9 | |
| Dielectric Loss Index | 0.300 - 0.400 | 0.300 - 0.400 | Average value: 0.340 Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 15.0 - 40.0 µm/m-°C | 8.33 - 22.2 µin/in-°F | Average value: 29.4 µm/m-°C Grade Count:11 |
| Thermal Conductivity | 0.290 - 0.300 W/m-K | 2.01 - 2.08 BTU-in/hr-ft²-°F | Average value: 0.296 W/m-K Grade Count:7 |
| Maximum Service Temperature, Air | 120 - 150 °C | 248 - 302 °F | Average value: 137 °C Grade Count:12 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 - 260 °C | 250 - 500 °F | Average value: 196 °C Grade Count:10 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | Average value: 164 °C Grade Count:9 |