- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 0.36
- 缺口冲击强度: 0.152
- 断裂伸长率 [%]: 74.0
- 弯曲强度 [MPa]: 51.0
- 弯曲模量 [MPa]: 6.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 - 1.54 g/cc | 0.0491 - 0.0556 lb/in³ | Average value: 1.43 g/cc Grade Count:10 |
| Water Absorption | 0.360 - 0.630 % | 0.360 - 0.630 % | Average value: 0.484 % Grade Count:10 |
| Linear Mold Shrinkage | 0.00233 - 0.0101 cm/cm | 0.00233 - 0.0101 in/in | Average value: 0.00554 cm/cm Grade Count:10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 57.0 - 89.0 | 57.0 - 89.0 | Average value: 75.3 Grade Count:10 |
| Tensile Strength, Ultimate | 51.0 - 69.0 MPa | 7400 - 10000 psi | Average value: 58.0 MPa Grade Count:10 |
| Elongation at Break | 0.680 - 1.26 % | 0.680 - 1.26 % | Average value: 0.927 % Grade Count:10 |
| Modulus of Elasticity | 6.60 - 9.40 GPa | 957 - 1360 ksi | Average value: 8.03 GPa Grade Count:10 |
| Flexural Yield Strength | 74.0 - 105 MPa | 10700 - 15200 psi | Average value: 85.4 MPa Grade Count:10 |
| Flexural Modulus | 6.60 - 8.60 GPa | 957 - 1250 ksi | Average value: 7.50 GPa Grade Count:10 |
| Compressive Yield Strength | 157 - 215 MPa | 22800 - 31200 psi | Average value: 189 MPa Grade Count:10 |
| Poissons Ratio | 0.330 - 0.360 | 0.330 - 0.360 | Average value: 0.346 Grade Count:5 |
| Shear Modulus | 2.70 - 3.26 GPa | 392 - 473 ksi | Average value: 2.96 GPa Grade Count:5 |
| Izod Impact, Notched | 0.152 - 0.209 J/cm | 0.285 - 0.392 ft-lb/in | Average value: 0.183 J/cm Grade Count:10 |
| Charpy Impact, Notched | 0.182 - 0.220 J/cm² | 0.866 - 1.05 ft-lb/in² | Average value: 0.194 J/cm² Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 8.30e+11 - 3.00e+13 ohm-cm | 8.30e+11 - 3.00e+13 ohm-cm | Average value: 1.04e+13 ohm-cm Grade Count:9 |
| Dielectric Constant | 4.40 - 7.00 | 4.40 - 7.00 | Average value: 5.74 Grade Count:9 |
| Dielectric Strength | 8.00 - 14.2 kV/mm | 203 - 361 kV/in | Average value: 11.2 kV/mm Grade Count:9 |
| Dissipation Factor | 0.0410 - 0.172 | 0.0410 - 0.172 | Average value: 0.0658 Grade Count:9 |
| Arc Resistance | 87.0 - 183 sec | 87.0 - 183 sec | Average value: 144 sec Grade Count:9 |
| Comparative Tracking Index | 175 V | 175 V | Average value: 175 V Grade Count:10 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 37.0 - 67.0 µm/m-°C @Temperature 40.0 - 130 °C | 20.6 - 37.2 µin/in-°F @Temperature 104 - 266 °F | Average value: 56.6 µm/m-°C Grade Count:7 |
| Thermal Conductivity | 0.370 - 0.460 W/m-K @Temperature 100 - 100 °C | 2.57 - 3.19 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F | Average value: 0.400 W/m-K Grade Count:4 |
| Maximum Service Temperature, Air | 183 - 207 °C | 361 - 405 °F | Average value: 196 °C Grade Count:10 |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 - 225 °C | 316 - 437 °F | Average value: 186 °C Grade Count:10 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:10 |
| Oxygen Index | 25.5 - 31.0 % | 25.5 - 31.0 % | Average value: 28.3 % Grade Count:4 |
| Shrinkage | 0.208 - 0.580 % | 0.208 - 0.580 % | Average value: 0.398 % Grade Count:10 |