- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.05
- 断裂伸长率 [%]: 102
- 弯曲强度 [MPa]: 50.0
- 弯曲模量 [MPa]: 6.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 - 1.55 g/cc | 0.0473 - 0.0560 lb/in³ | Average value: 1.42 g/cc Grade Count:8 |
| Water Absorption | 0.0500 - 0.900 % | 0.0500 - 0.900 % | Average value: 0.289 % Grade Count:4 |
| Linear Mold Shrinkage | 0.000 - 0.00200 cm/cm | 0.000 - 0.00200 in/in | Average value: 0.000760 cm/cm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 50.0 - 258 MPa | 7250 - 37400 psi | Average value: 119 MPa Grade Count:8 |
| Modulus of Elasticity | 20.0 - 62.0 GPa | 2900 - 8990 ksi | Average value: 38.2 GPa Grade Count:3 |
| Flexural Yield Strength | 102 - 521 MPa | 14800 - 75600 psi | Average value: 253 MPa Grade Count:8 |
| Flexural Modulus | 6.30 - 44.8 GPa | 914 - 6500 ksi | Average value: 21.8 GPa Grade Count:8 |
| Compressive Yield Strength | 164 - 359 MPa | 23800 - 52100 psi | Average value: 258 MPa Grade Count:7 |
| Compressive Modulus | 8.41 - 17.0 GPa | 1220 - 2470 ksi | Average value: 11.9 GPa Grade Count:3 |
| Charpy Impact Unnotched | 1.09 - 1.70 J/cm² | 5.19 - 8.09 ft-lb/in² | Average value: 1.38 J/cm² Grade Count:3 |
| Charpy Impact, Notched | 0.200 - 0.300 J/cm² | 0.952 - 1.43 ft-lb/in² | Average value: 0.248 J/cm² Grade Count:4 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 1.00 - 10.0 µm/m-°C | 0.556 - 5.56 µin/in-°F | Average value: 5.67 µm/m-°C Grade Count:3 |
| CTE, linear, Transverse to Flow | 20.0 - 40.0 µm/m-°C | 11.1 - 22.2 µin/in-°F | Average value: 26.5 µm/m-°C Grade Count:3 |
| Shrinkage | 0.000 - 0.100 % | 0.000 - 0.100 % | Average value: 0.0300 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Shelf Life | 2.00 - 6.00 Month @Temperature -17.8 - 4.44 °C | 2.00 - 6.00 Month @Temperature 0.000 - 40.0 °F | Average value: 4.00 Month Grade Count:1 |