- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.4
- 缺口冲击强度: 0.214
- 弯曲强度 [MPa]: 59.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.500 g/cc | 0.0181 lb/in³ | ASTM D1895 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | ASTM D638 |
| Tensile Modulus | 7.60 GPa | 1100 ksi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | |
| Compressive Strength | 221 MPa | 32100 psi | ASTM D695 |
| Izod Impact, Notched | 0.214 J/cm | 0.401 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 6.5 @Frequency 1e+6 Hz | 6.5 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 9.80 kV/mm | 249 kV/in | Step by step; ASTM D149 |
| 11.8 kV/mm | 300 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.080 @Frequency 1e+6 Hz | 0.080 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 150 °C @Thickness 3.0 mm | 302 °F @Thickness 0.12 in | UL Temperature Index |
| Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.5 mm | HB @Thickness 0.059 in | |
| HB @Thickness 3.0 mm | HB @Thickness 0.12 in | ||
| V-0 @Thickness 6.0 mm | V-0 @Thickness 0.24 in | ||