- 密度 [g/cm3]: 1.77
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.4
- 弯曲强度 [MPa]: 138.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.770 g/cc | 0.0278 lb/in³ | ASTM D1895 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 120 | 120 | |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ASTM D638 |
| Tensile Modulus | 18.6 GPa | 2700 ksi | ASTM D638 |
| Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
| Compressive Strength | 289 MPa | 41900 psi | ASTM D695 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.3 @Frequency 1e+6 Hz | 4.3 @Frequency 1e+6 Hz | ASTM D150 |
| Dielectric Strength | 15.7 kV/mm | 399 kV/in | Step by step; ASTM D149 |
| 17.7 kV/mm | 450 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 13.3 µin/in-°F @Temperature 73.4 - 140 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C | 302 °F | |
| Flammability, UL94 | V-1 @Thickness 0.800 mm | V-1 @Thickness 0.0315 in | |
| V-1 @Thickness 0.800 mm | V-1 @Thickness 0.0315 in | ||
| V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | ||
| Processing Properties | Metric | English | Comments |
| Shelf Life | 12.0 Month | 12.0 Month | |