- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 0.11
- 缺口冲击强度: 0.4
- 弯曲模量 [MPa]: 10.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ASTM D1895 | ||
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.11 % @Time 86400 sec | 0.11 % @Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 83 | 83 | ASTM D785 | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ASTM D638 | ||
| Flexural Strength | 140 MPa | 20300 psi | ASTM D790 | ||
| Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 | ||
| Compressive Strength | 210 MPa | 30500 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 11.5 kV/mm @Frequency 60.0 Hz | 292 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 15.0 kV/mm @Frequency 60.0 Hz | 381 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Arc Resistance | 50 sec | 50 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 13.0 µm/m-°C | 7.22 µin/in-°F | ASTM E831 | ||
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | ASTM C518 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | As Molded; ASTM D648A | ||
| >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| V-1 @Thickness 3.20 mm | V-1 @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||