- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.08
- 缺口冲击强度: 3.0
- 弯曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | ISO 60 | ||
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.080 % | 0.080 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0025 cm/cm | 0.0025 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 100 | 100 | ISO 2039/2 | ||
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 | ||
| Flexural Strength | 175 MPa | 25400 psi | ISO 178 | ||
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178 | ||
| Compressive Strength | 350 MPa | 50800 psi | ISO 604 | ||
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 14.0 kV/mm @Frequency 60.0 Hz | 356 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | ||
| Arc Resistance | 150 sec | 150 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ASTM E831 | ||
| Thermal Conductivity | 0.410 W/m-K | 2.85 BTU-in/hr-ft²-°F | ASTM C518 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL Temperature Index; UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | As Molded; ISO 75A | ||
| >= 282 °C | >= 540 °F | Post Baked; ISO 75A | |||
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | |||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||||
| Descriptive Properties | |||||
| Colors | Black, Green | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||