- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 - 1.75 g/cc | 0.0578 - 0.0632 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.700 - 0.800 g/cc | 0.0253 - 0.0289 lb/in³ | IS 867-1963 |
| Water Absorption | 0.15 - 0.25 % | 0.15 - 0.25 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 50.0 - 60.0 MPa | 7250 - 8700 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 80.0 - 90.0 MPa | 11600 - 13100 psi | IS 867-1963 |
| Izod Impact, Notched | 0.400 - 0.500 J/cm | 0.749 - 0.937 ft-lb/in | IS 13411-1992 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 1.08 - 1.33 min | 0.0181 - 0.0222 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |