- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.1
- 缺口冲击强度: 0.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 - 1.70 g/cc | 0.0578 - 0.0614 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.750 - 0.850 g/cc | 0.0271 - 0.0307 lb/in³ | IS 867-1963 |
| Water Absorption | 0.10 - 0.15 % | 0.10 - 0.15 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0020 - 0.0035 cm/cm | 0.0020 - 0.0035 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 - 56.0 MPa | 6670 - 8120 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 60.0 - 65.0 MPa | 8700 - 9430 psi | IS 867-1963 |
| Izod Impact, Notched | 0.200 - 0.300 J/cm | 0.375 - 0.562 ft-lb/in | IS 13411-1992 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 170 °C | 320 - 338 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 1.00 - 1.17 min | 0.0167 - 0.0194 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |