- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.17
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 - 1.68 g/cc | 0.0560 - 0.0607 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.740 - 0.840 g/cc | 0.0267 - 0.0303 lb/in³ | IS 867-1963 |
| Water Absorption | 0.20 - 0.30 % | 0.20 - 0.30 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0024 - 0.0036 cm/cm | 0.0024 - 0.0036 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 28.0 - 35.0 MPa | 4060 - 5080 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 32.0 - 45.0 MPa | 4640 - 6530 psi | IS 867-1963 |
| Izod Impact, Notched | 0.170 - 0.270 J/cm | 0.318 - 0.506 ft-lb/in | IS 13411-1992 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 14.7 - 29.4 MPa | 2130 - 4260 psi | Mold Pressure |
| Cure Time | 0.550 - 0.750 min | 0.00917 - 0.0125 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |