Momentive Performance Materials PF 4010 Phenolic Formaldehyde Resin, Improved Electrical Properties,

Momentive Performance Materials PF 4010 Phenolic Formaldehyde Resin, Improved Electrical Properties, 物性表: Momentive Performance Materials PF 4010 Phenolic Formaldehyde Resin, Improved Electrical Properties,物性表及特性介绍,Momentive Performance Materials PF 4010 Phenolic Formaldehyde Resin, Improved Electrical Properties,注塑参数详情,如需Momentive Performance Materials PF 4010 Phenolic Formaldehyde Resin, Improved Electrical Properties,下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.7
  • 弯曲模量 [MPa]: 12.0
 
Physical PropertiesMetricEnglishComments
Density 1.70 g/cc0.0614 lb/in³ISO 1183
Apparent Bulk Density 0.700 g/cc0.0253 lb/in³ISO 60
Linear Mold Shrinkage, Flow 0.0040 cm/cm0.0040 in/inInjection molding; ISO 2577
 
Mechanical PropertiesMetricEnglishComments
Flexural Strength 110 MPa16000 psi2 mm/min; ISO 178
Flexural Modulus 12.0 GPa1740 ksiISO 178
Charpy Impact Unnotched 0.800 J/cm²
@Temperature 23.0 °C
3.81 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1/2 eU
Charpy Impact, Notched 0.250 J/cm²
@Temperature 23.0 °C
1.19 ft-lb/in²
@Temperature 73.4 °F
ISO 179-1/2 eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+10 ohm-cm1.00e+10 ohm-cmIEC 60093
Surface Resistance 1.00e+9 ohm1.00e+9 ohmIEC 60093
Dielectric Strength 25.0 kV/mm
@Thickness 1.00 mm
635 kV/in
@Thickness 0.0394 in
IEC 60243-P1
Dissipation Factor 0.20
@Frequency 100 Hz
0.20
@Frequency 100 Hz
IEC 60250
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 8.0 MPa 160 °C320 °FISO 75-2
Shrinkage 0.15 %0.15 %Injection molding, 168 hours/110°C; ISO 2577
 
Processing PropertiesMetricEnglishComments
Feed Temperature 60.0 - 75.0 °C140 - 167 °FInjection molding
Nozzle Temperature 80.0 - 100 °C176 - 212 °FInjection molding
Melt Temperature 80.0 - 100 °C176 - 212 °FInjection molding
Mold Temperature 160 - 190 °C320 - 374 °FInjection molding
 160 - 190 °C320 - 374 °FCompression molding
Injection Pressure >= 15.0 MPa>= 2180 psiCompression and injection cavity mold pressure
Back Pressure 0.500 - 2.00 MPa72.5 - 290 psiInjection molding
Cure Time 0.167 - 0.333 min0.00278 - 0.00556 hourPer 1 mm of wall thickness, injection molding
 0.333 - 0.667 min0.00556 - 0.0111 hourPer 1 mm of wall thickness, compression molding
 
Descriptive Properties
Chromatic SpectrumAll Colors
Creep Rupture StrengthVery Good
Holding PressureApproximately 40-60% of injection pressure
Media ResistanceVery Good
Moisture Absorption30 mgISO 62, 24 hours at 23°C
Reserves by Peak TemperatureVery High
Thermal ExpansionVery Slight

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-34861.html

免责声明: 本文 Momentive Performance Materials PF 4010 Phenolic Formaldehyde Resin, Improved Electrical Properties, 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4