- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.15
- 缺口冲击强度: 0.22
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 - 1.60 g/cc | 0.0524 - 0.0578 lb/in³ | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.680 - 0.800 g/cc | 0.0246 - 0.0289 lb/in³ | IS 867-1963 |
| Water Absorption | 0.15 - 0.30 % | 0.15 - 0.30 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0045 - 0.0055 cm/cm | 0.0045 - 0.0055 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 39.0 - 46.0 MPa | 5660 - 6670 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 66.0 - 75.0 MPa | 9570 - 10900 psi | 2mm/min.; IS 867-1963 |
| Izod Impact, Notched | 0.220 - 0.300 J/cm | 0.412 - 0.562 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.2e+11 - 1.0e+12 ohm-cm | 3.2e+11 - 1.0e+12 ohm-cm | IS 3396-1979 |
| Surface Resistance | 3.2e+10 - 3.2e+11 ohm | 3.2e+10 - 3.2e+11 ohm | IS 3396-1979 |
| Dielectric Strength | 6.50 - 7.50 kV/mm @Temperature 90.0 °C | 165 - 191 kV/in @Temperature 194 °F | IS 2584-1963 |
| Comparative Tracking Index | >= 150 V | >= 150 V | 2824-1975 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 15.68 - 34.3 MPa | 2274 - 4970 psi | Mold Pressure |
| Cure Time | 0.333 - 0.500 min | 0.00556 - 0.00833 hour | per mm |
| Shelf Life | 12.0 Month | 12.0 Month | 10-25°C |