- 密度 [g/cm3]: 0.0561
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0561 g/cc | 0.00203 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 1.93 MPa | >= 280 psi | Bare, min |
| 2.69 MPa | 390 psi | Bare, typ | |
| >= 2.76 MPa | >= 400 psi | Stabilized, min | |
| 3.14 MPa | 455 psi | Stabilized, typ | |
| Compressive Modulus | 0.317 GPa | 46.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0345 GPa | 5.00 ksi | Plate Shear, W Direction, typ |
| 0.0689 GPa | 10.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 0.689 MPa | >= 100 psi | Plate Shear, W Direction, min |
| 0.862 MPa | 125 psi | Plate Shear, W Direction, typ | |
| >= 1.24 MPa | >= 180 psi | Plate Shear, L Direction, min | |
| 1.79 MPa | 260 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |