- 密度 [g/cm3]: 0.112
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.112 g/cc | 0.00405 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 5.86 MPa | >= 850 psi | Bare, min |
| >= 6.83 MPa | >= 990 psi | Stabilized, min | |
| 7.93 MPa | 1150 psi | Bare, typ | |
| 8.48 MPa | 1230 psi | Stabilized, typ | |
| Compressive Modulus | 0.579 GPa | 84.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0965 GPa | 14.0 ksi | Plate Shear, L Direction, typ |
| 0.138 GPa | 20.0 ksi | Plate Shear, W Direction, typ | |
| Shear Strength | >= 2.14 MPa | >= 310 psi | Plate Shear, L Direction, min |
| >= 2.41 MPa | >= 350 psi | Plate Shear, W Direction, min | |
| 2.72 MPa | 395 psi | Plate Shear, L Direction, typ | |
| 3.10 MPa | 450 psi | Plate Shear, W Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | High strength retained |