- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.285
- 缺口冲击强度: 0.205
- 弯曲强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 9.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.610 g/cc | 0.0220 lb/in³ | ASTM D1895 |
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM D792 |
| Water Absorption | 0.285 % | 0.285 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0057 cm/cm | 0.0057 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 67 | 67 | ASTM D785 |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 0.71 % | 0.71 % | ASTM D638 |
| Tensile Modulus | 11.8 GPa | 1710 ksi | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 9.90 GPa | 1440 ksi | ASTM D790 |
| Compressive Strength | 142 MPa | 20600 psi | ASTM D695 |
| Izod Impact, Notched | 0.205 J/cm | 0.384 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.217 J/cm² | 1.03 ft-lb/in² | ASTM D256 |
| Impact | 132 | 132 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.30e+11 ohm-cm | 6.30e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 7.6 | 7.6 | ASTM D150 |
| Dielectric Strength | 5.50 kV/mm | 140 kV/in | Step by Step; ASTM D149 |
| 7.80 kV/mm | 198 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.114 | 0.114 | ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 600 V | 600 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 0.610 W/m-K @Temperature 100 °C | 4.23 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 144 °C | 291 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.00 mm | V-0 @Thickness 0.0394 in | |
| Oxygen Index | 36 % | 36 % | ASTM D2863 |
| Shrinkage | 0.95 % | 0.95 % | 240 hr, 105ºC; ASTM D1299 |