- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 0.43
- 缺口冲击强度: 0.163
- 弯曲强度 [MPa]: 59.0
- 弯曲模量 [MPa]: 7.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.640 g/cc | 0.0231 lb/in³ | ASTM D1895 |
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.43 % | 0.43 % | ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 83 | 83 | ASTM D785 |
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 0.86 % | 0.86 % | ASTM D638 |
| Tensile Modulus | 8.20 GPa | 1190 ksi | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | ASTM D790 |
| Compressive Strength | 198 MPa | 28700 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | ASTM D638 |
| Shear Modulus | 3.08 GPa | 447 ksi | Calculated |
| Izod Impact, Notched | 0.163 J/cm | 0.305 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.178 J/cm² | 0.847 ft-lb/in² | ASTM D256 |
| Impact | 98 | 98 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.20e+11 ohm-cm | 2.20e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.2 | 5.2 | ASTM D150 |
| Dielectric Strength | 9.30 kV/mm | 236 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.083 | 0.083 | ASTM D150 |
| Arc Resistance | 144 sec | 144 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 57.0 µm/m-°C @Temperature 40.0 - 130 °C | 31.7 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.400 W/m-K @Temperature 100 °C | 2.78 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 201 °C | 394 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 27 % | 27 % | ASTM D2863 |
| Shrinkage | 0.42 % | 0.42 % | 72 hr, 120ºC; ASTM D1299 |