- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.54
- 缺口冲击强度: 0.182
- 弯曲强度 [MPa]: 56.0
- 弯曲模量 [MPa]: 8.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.710 g/cc | 0.0257 lb/in³ | ASTM D1895 |
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.54 % | 0.54 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0032 cm/cm | 0.0032 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 68 | 68 | ASTM D785 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 0.81 % | 0.81 % | ASTM D638 |
| Tensile Modulus | 8.80 GPa | 1280 ksi | ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 8.10 GPa | 1170 ksi | ASTM D790 |
| Compressive Strength | 165 MPa | 23900 psi | ASTM D695 |
| Poissons Ratio | 0.35 | 0.35 | ASTM D638 |
| Shear Modulus | 3.26 GPa | 473 ksi | Calculated |
| Izod Impact, Notched | 0.182 J/cm | 0.341 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.197 J/cm² | 0.938 ft-lb/in² | ASTM D256 |
| Impact | 119 | 119 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.40e+13 ohm-cm | 2.40e+13 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.6 | 5.6 | ASTM D150 |
| Dielectric Strength | 13.7 kV/mm | 348 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.046 | 0.046 | ASTM D150 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 55.0 µm/m-°C @Temperature 40.0 - 130 °C | 30.6 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.370 W/m-K @Temperature 100 °C | 2.57 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 191 °C | 376 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Oxygen Index | 25.5 % | 25.5 % | ASTM D2863 |
| Shrinkage | 0.36 % | 0.36 % | 72 hr, 120ºC; ASTM D1299 |