- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 0.52
- 缺口冲击强度: 0.2
- 弯曲强度 [MPa]: 69.0
- 弯曲模量 [MPa]: 6.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.580 g/cc | 0.0210 lb/in³ | ASTM D1895 |
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Water Absorption | 0.52 % | 0.52 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0069 cm/cm | 0.0069 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 78 | 78 | ASTM D785 |
| Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 1.26 % | 1.26 % | ASTM D638 |
| Tensile Modulus | 6.60 GPa | 957 ksi | ASTM D638 |
| Flexural Strength | 105 MPa | 15200 psi | ASTM D790 |
| Flexural Modulus | 6.70 GPa | 972 ksi | ASTM D790 |
| Compressive Strength | 209 MPa | 30300 psi | ASTM D695 |
| Izod Impact, Notched | 0.200 J/cm | 0.375 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.182 J/cm² | 0.866 ft-lb/in² | ASTM D256 |
| Impact | 116 | 116 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 190 °C | 374 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |
| Shrinkage | 0.51 % | 0.51 % | 72 hr, 120ºC; ASTM D1299 |