- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.215
- 缺口冲击强度: 0.171
- 弯曲强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.690 g/cc | 0.0249 lb/in³ | ASTM D1895 |
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| Water Absorption | 0.215 % | 0.215 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0052 cm/cm | 0.0052 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 87 | 87 | ASTM D785 |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 0.80 % | 0.80 % | ASTM D638 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ASTM D638 |
| Flexural Strength | 98.0 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Compressive Strength | 208 MPa | 30200 psi | ASTM D695 |
| Poissons Ratio | 0.34 | 0.34 | ASTM D638 |
| Shear Modulus | 3.36 GPa | 487 ksi | Calculated |
| Izod Impact, Notched | 0.171 J/cm | 0.320 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ASTM D256 |
| Impact | 104 | 104 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 7.10e+11 ohm-cm | 7.10e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.3 | 5.3 | ASTM D150 |
| Dielectric Strength | 12.3 kV/mm | 312 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.056 | 0.056 | ASTM D150 |
| Arc Resistance | 144 sec | 144 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 µm/m-°C @Temperature 40.0 - 130 °C | 36.1 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.440 W/m-K @Temperature 100 °C | 3.05 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 204 °C | 399 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 27.3 % | 27.3 % | ASTM D2863 |
| Shrinkage | 0.199 % | 0.199 % | 72 hr, 120ºC; ASTM D1299 |