- 密度 [g/cm3]: 1.58
- 吸水率 [%]: 0.179
- 缺口冲击强度: 0.166
- 弯曲强度 [MPa]: 49.0
- 弯曲模量 [MPa]: 8.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.630 g/cc | 0.0228 lb/in³ | ASTM D1895 |
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| Water Absorption | 0.179 % | 0.179 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0076 cm/cm | 0.0076 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 73 | 73 | ASTM D785 |
| Tensile Strength, Ultimate | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 0.58 % | 0.58 % | ASTM D638 |
| Tensile Modulus | 10.3 GPa | 1490 ksi | ASTM D638 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
| Compressive Strength | 156 MPa | 22600 psi | ASTM D695 |
| Poissons Ratio | 0.34 | 0.34 | ASTM D638 |
| Shear Modulus | 3.84 GPa | 557 ksi | Calculated |
| Izod Impact, Notched | 0.166 J/cm | 0.311 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.182 J/cm² | 0.866 ft-lb/in² | ASTM D256 |
| Impact | 98 | 98 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+11 ohm-cm | 2.00e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.7 | 5.7 | ASTM D150 |
| Dielectric Strength | 10.6 kV/mm | 269 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.067 | 0.067 | ASTM D150 |
| Arc Resistance | 182 sec | 182 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 46.0 µm/m-°C @Temperature 40.0 - 130 °C | 25.6 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.540 W/m-K @Temperature 100 °C | 3.75 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 202 °C | 396 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Oxygen Index | 27.4 % | 27.4 % | ASTM D2863 |
| Shrinkage | 0.271 % | 0.271 % | 72 hr, 120ºC; ASTM D1299 |