- 密度 [g/cm3]: 1.56
- 吸水率 [%]: 0.146
- 缺口冲击强度: 0.243
- 弯曲强度 [MPa]: 47.0
- 弯曲模量 [MPa]: 9.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.680 g/cc | 0.0246 lb/in³ | ASTM D1895 |
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Water Absorption | 0.146 % | 0.146 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0042 cm/cm | 0.0042 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 73 | 73 | ASTM D785 |
| Tensile Strength, Ultimate | 47.0 MPa | 6820 psi | ASTM D638 |
| Elongation at Break | 0.68 % | 0.68 % | ASTM D638 |
| Tensile Modulus | 9.10 GPa | 1320 ksi | ASTM D638 |
| Flexural Strength | 86.0 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 9.20 GPa | 1330 ksi | ASTM D790 |
| Compressive Strength | 157 MPa | 22800 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | ASTM D638 |
| Shear Modulus | 3.42 GPa | 496 ksi | Calculated |
| Izod Impact, Notched | 0.243 J/cm | 0.455 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.247 J/cm² | 1.18 ft-lb/in² | ASTM D256 |
| Impact | 138 | 138 | J/m drop Ball Impact; PLENCO |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.10e+11 ohm-cm | 3.10e+11 ohm-cm | ASTM D247 |
| Dielectric Constant | 5.5 | 5.5 | ASTM D150 |
| Dielectric Strength | 11.6 kV/mm | 295 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.054 | 0.054 | ASTM D150 |
| Arc Resistance | 184 sec | 184 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 51.0 µm/m-°C @Temperature 40.0 - 130 °C | 28.3 µin/in-°F @Temperature 104 - 266 °F | TMA; ASTM E831 |
| Thermal Conductivity | 0.570 W/m-K @Temperature 100 °C | 3.96 BTU-in/hr-ft²-°F @Temperature 212 °F | ASTM E1461 |
| Maximum Service Temperature, Air | 196 °C | 385 °F | Heat Resistance; ASTM D570D |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm | V-0 @Thickness 0.236 in | |
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Shrinkage | 0.171 % | 0.171 % | 72 hr, 120ºC; ASTM D1299 |