- 拉伸强度 [MPa]: 179.0
- 弯曲模量 [MPa]: 16.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | 8HS form; ASTM D792 | ||
| Volatiles | 2.0 - 8.0 % @Temperature 163 °C | 2.0 - 8.0 % @Temperature 325 °F | 5 min | ||
| Thickness | 406 microns | 16.0 mil | per ply, 8HS form | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Barcol | 75 | 75 | 8HS form; ASTM D2583 | ||
| Tensile Strength, Yield | 179 MPa @Temperature 23.9 °C | 26000 psi @Temperature 75.0 °F | 0° Direction, Dry; 8HS form; ASTM D638 | ||
| Tensile Modulus | 16.5 GPa @Temperature 23.9 °C | 2400 ksi @Temperature 75.0 °F | 0° Direction, Dry; 8HS form; ASTM D638 | ||
| Flexural Strength | 228 MPa @Temperature 23.9 °C | 33000 psi @Temperature 75.0 °F | Dry; 8HS form; ASTM D790 | ||
| Flexural Modulus | 16.5 GPa @Temperature 23.9 °C | 2400 ksi @Temperature 75.0 °F | Dry; 8HS form; ASTM D790 | ||
| Compressive Strength | 317 MPa @Temperature 23.9 °C | 46000 psi @Temperature 75.0 °F | Dry; 8HS form; ASTM D695 | ||
| Compressive Modulus | 15.2 GPa @Temperature 23.9 °C | 2200 ksi @Temperature 75.0 °F | Dry; 8HS form; ASTM D695 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 7.20 µm/m-°C @Temperature 204 °C | 4.00 µin/in-°F @Temperature 400 °F | with ply; 8HS form; ASTM D696 | ||
| 12.2 µm/m-°C @Temperature 204 °C | 6.80 µin/in-°F @Temperature 400 °F | x-ply; 8HS form; ASTM D696 | |||
| Specific Heat Capacity | 1.17 J/g-°C | 0.280 BTU/lb-°F | 8HS form; ASTM C351 | ||
| Thermal Conductivity | 0.0850 W/m-K @Temperature 149 °C | 0.590 BTU-in/hr-ft²-°F @Temperature 300 °F | x-ply; 8HS form; ASTM C177 | ||
| 0.133 W/m-K @Temperature 149 °C | 0.920 BTU-in/hr-ft²-°F @Temperature 300 °F | with-ply; 8HS form; ASTM C177 | |||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Fabric Area Weight (g/m²) | 270 | ||||
| Filler Content (%) | 8-16 | ||||
| Prepreg Resin Content (%) | 31-37 | ||||
| Resin Flow (%) | 5-25 | 325°F, 150psi | |||