- 拉伸强度 [MPa]: 53.8
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Volatiles | 2.0 - 4.0 % @Temperature 135 °C | 2.0 - 4.0 % @Temperature 275 °F | 8 min | ||
| Thickness | 381 microns | 15.0 mil | nominal, cured, per ply | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 53.8 MPa @Temperature 23.9 °C | 7800 psi @Temperature 75.0 °F | ±45° Direction, Dry; ASTM D638 | ||
| 262 MPa @Temperature 23.9 °C | 38000 psi @Temperature 75.0 °F | 0° Direction, Dry; ASTM D638 | |||
| Elongation at Yield | 7.2 % @Temperature 23.9 °C | 7.2 % @Temperature 75.0 °F | Tensile; Dry; ASTM D638 | ||
| Tensile Modulus | 2.76 GPa @Temperature 23.9 °C | 400 ksi @Temperature 75.0 °F | ±45° Direction, Dry; ASTM D638 | ||
| 12.4 GPa @Temperature 23.9 °C | 1800 ksi @Temperature 75.0 °F | 0° Direction, Dry; ASTM D638 | |||
| Flexural Strength | 207 MPa @Temperature 23.9 °C | 30000 psi @Temperature 75.0 °F | Dry; ASTM D790 | ||
| Flexural Modulus | 11.0 GPa @Temperature 23.9 °C | 1600 ksi @Temperature 75.0 °F | Dry; ASTM D790 | ||
| Compressive Strength | 131 MPa @Temperature 23.9 °C | 19000 psi @Temperature 75.0 °F | Dry; ASTM D695 | ||
| Compressive Modulus | 12.4 GPa @Temperature 23.9 °C | 1800 ksi @Temperature 75.0 °F | Dry; ASTM D695 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 6.00 Month @Temperature 4.44 °C | 6.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Resin Flow (%) | 1-7 | 260°F, 150psi | |||
| Resin Solids Content (%) | 30-36 | ||||