- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.6
- 缺口冲击强度: 1.103
- 弯曲强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792A |
| Water Absorption | 0.60 % | 0.60 % | 24 hours R.T. ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | Positive Mold; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D651 |
| Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Strength | 150 MPa | 21800 psi | ASTM D695 |
| Izod Impact, Notched | 1.103 J/cm | 2.066 ft-lb/in | ASTM D256A |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 12.8 kV/mm | 325 kV/in | Short Time; Dry; ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 °C | 10.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 177 °C | 351 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 150 - 175 °C | 302 - 347 °F | |