- 密度 [g/cm3]: 1.88
- 缺口冲击强度: 4.5
- 弯曲模量 [MPa]: 20.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | Powder Density; ISO 60 | ||
| Density | 1.88 g/cc | 0.0679 lb/in³ | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | Compression Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell E | 95 | 95 | ISO 2039/2 | ||
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527 | ||
| Flexural Strength | 135 MPa | 19600 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 20.0 GPa | 2900 ksi | ISO 178 | ||
| Compressive Strength | 265 MPa | 38400 psi | ISO 604 | ||
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 13.5 kV/mm | 343 kV/in | 60Hz, Short Time, dry; ASTM D149 | ||
| Arc Resistance | 185 sec | 185 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C @Temperature 20.0 °C | 9.44 µin/in-°F @Temperature 68.0 °F | ASTM E-831 | ||
| CTE, linear, Transverse to Flow | 39.0 µm/m-°C @Temperature 20.0 °C | 21.7 µin/in-°F @Temperature 68.0 °F | ASTM E-831 | ||
| Thermal Conductivity | 0.740 W/m-K | 5.14 BTU-in/hr-ft²-°F | ASTM C-518 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | UL 746B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | Post Baked; ISO 75 A | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Flake | ||||
| Main Filler | Glass Fiber | ||||
| Molding Method | Compression, transfer, injection | ||||