- 密度 [g/cm3]: 1.99
- 吸水率 [%]: 0.05
- 弯曲模量 [MPa]: 21.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | ISO 60 | ||
| Density | 1.99 g/cc | 0.0719 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.050 % | 0.050 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0018 cm/cm | 0.0018 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 119 MPa | 17300 psi | ISO 527-1 | ||
| Elongation at Break | 0.59 % | 0.59 % | ISO 527-1 | ||
| Tensile Modulus | 23.0 GPa | 3340 ksi | ISO 527-1 | ||
| Flexural Strength | 240 MPa | 34800 psi | ISO 178 | ||
| Flexural Modulus | 21.0 GPa | 3050 ksi | ISO 178 | ||
| Compressive Strength | 434 MPa | 62900 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.36 J/cm² | 6.47 ft-lb/in² | ISO 179-1 | ||
| Charpy Impact, Notched | 0.290 J/cm² | 1.38 ft-lb/in² | ISO 179-1 | ||
| Coefficient of Friction, Dynamic | 0.54 | 0.54 | |||
| Coefficient of Friction, Static | 0.56 | 0.56 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.10e+14 ohm-cm | 2.10e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 2.50e+12 ohm | 2.50e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 225 V | 225 V | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C | 8.89 µin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 24.0 µm/m-°C | 13.3 µin/in-°F | TMA | ||
| Thermal Conductivity | 0.510 W/m-K | 3.54 BTU-in/hr-ft²-°F | ASTM E1461 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 250 °C | >= 482 °F | ISO 75 Af | ||
| Deflection Temperature at 8.0 MPa | 178 °C | 352 °F | ISO 75 Cf | ||
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||||
| Shrinkage | 0.040 % | 0.040 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||