- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 0.8
- 缺口冲击强度: 0.29
- 断裂伸长率 [%]: 62.0
- 弯曲强度 [MPa]: 46.0
- 弯曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.450 g/cc | 0.0163 lb/in³ | ASTM D1895 |
| Water Absorption | 0.80 % | 0.80 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | ASTM D638 |
| Flexural Yield Strength | 62.0 MPa | 8990 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Compressive Yield Strength | 172 MPa | 24900 psi | ASTM D695 |
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.00e+11 ohm-cm | 3.00e+11 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.3 | 5.3 | 1MHz; ASTM D150 |
| 8.5 | 8.5 | 60 Hz; ASTM D150 | |
| Dielectric Strength | 13.2 kV/mm | 335 kV/in | ASTM D149 |
| Dissipation Factor | 0.050 | 0.050 | 1 MHz; ASTM D150 |
| 0.24 | 0.24 | 60 Hz; ASTM D150 | |
| Comparative Tracking Index | 138 V | 138 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| Flammability, UL94 | HB | HB | 3.18mm |
| HB | HB | 3.18mm | |