- 密度 [g/cm3]: 1.04
- 缺口冲击强度: 2.7
- 弯曲强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 0.600
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 24.0 MPa | 3480 psi | ASTM D638/D412 |
| Elongation at Break | 135 % | 135 % | ASTM D638/D412 |
| Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
| Izod Impact, Notched | 2.70 J/cm | 5.06 ft-lb/in | ASTM D256 |
| Tear Strength | 82.0 kN/m | 468 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 110 µm/m-°C @Temperature 20.0 °C | 61.1 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Flammability, UL94 | HB @Thickness 3.18 mm | HB @Thickness 0.125 in | |
| HB @Thickness 3.18 mm | HB @Thickness 0.125 in | ||