- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 2.8
- 弯曲强度 [MPa]: 28.0
- 弯曲模量 [MPa]: 0.470
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | 2.8 % | 2.8 % | 240 hours; Bayer Test |
| Linear Mold Shrinkage | 0.0056 cm/cm | 0.0056 in/in | Bayer Test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 28.0 MPa | 4060 psi | ASTM D638/D412 |
| Elongation at Break | 105 % | 105 % | ASTM D638/D412 |
| Flexural Modulus | 0.470 GPa | 68.2 ksi | ASTM D790 |
| Tear Strength | 80.0 kN/m | 456 pli | Die C; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | <= 76.0 µm/m-°C @Temperature 20.0 °C | <= 42.2 µin/in-°F @Temperature 68.0 °F | ASTM D696 |