Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 2.40 g/cc | 2.40 g/cc | ASTM D792 | ||
Viscosity | 1.70e+6 cP | 1.70e+6 cP | |||
Deformation | 30 % | 30 % | 141.8 N/cm; ASTM D575 Modified | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore A | 75 - 79 | 75 - 79 | ASTM DD2240 | ||
Tensile Strength at Break | 3.10 - 3.45 MPa | 450 - 500 psi | ASTM D412 | ||
Elongation at Break | 125 % | 125 % | ASTM D412 | ||
Compression Set | 30 % @Temperature 70.0 °C, Time 79200 sec | 30 % @Temperature 158 °F, Time 22.0 hour | ASTM D395 Method B | ||
40 % @Temperature 85.0 °C, Time 79200 sec | 40 % @Temperature 185 °F, Time 22.0 hour | ASTM D395 Method B | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 0.020 ohm-cm | 0.020 ohm-cm | Initial; Chomerics MAT-1002 | ||
0.030 ohm-cm | 0.030 ohm-cm | Chomerics MAT-1002 | |||
0.040 ohm-cm | 0.040 ohm-cm | Aged; Chomerics MAT-1002 | |||
Shielding Effectiveness | 65 - 70 dB @Frequency 2.00e+8 - 1.20e+10 Hz | 65 - 70 dB @Frequency 2.00e+8 - 1.20e+10 Hz | |||
Thermal Properties | Metric | English | Comments | ||
Maximum Service Temperature, Air | 150 °C | 302 °F | |||
Flammability, UL94 | V-0 | V-0 | |||
Processing Properties | Metric | English | Comments | ||
Cure Time | 30.0 min @Temperature 150 °C | 0.500 hour @Temperature 302 °F | Tack Free Time | ||
30.0 min @Temperature 150 °C | 0.500 hour @Temperature 302 °F | Handling Time | |||
30.0 min @Temperature 150 °C | 0.500 hour @Temperature 302 °F | Full Cure | |||
Shelf Life | 6.00 Month @Temperature -12.0 - -8.00 °C | 6.00 Month @Temperature 10.4 - 17.6 °F | Chomerics | ||
Descriptive Properties | |||||
Adhesion | 10-12 N/cm | Trivalent Chromate Coating on Aluminum | |||
Binder | Silicone | ||||
Cure System | Thermal | ||||
Filler | Nickel-plated graphite (Ni/C) | ||||
Flow Rate | 0.85 - 1.15 grams/min | Chomerics - MAT-1200 | |||
Galvanic Corrosion | 32 mg | Resistance Against Aluminum; Chomerics TM-100 | |||
Number of Components | 1 |