| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.20 g/cc | 2.20 g/cc | ASTM D792 | ||
| Thickness | 508 - 5080 microns | 20.0 - 200 mil | ASTM D374 | ||
| Deformation | 10 % @Thickness 3.17 mm, Pressure 0.0345 MPa | 10 % @Thickness 0.125 in, Pressure 5.00 psi | 0.5" diameter probe, 0.025 in/min rate; ASTM C165 MOD | ||
| 15 % @Thickness 3.17 mm, Pressure 0.0689 MPa | 15 % @Thickness 0.125 in, Pressure 10.0 psi | 0.5" diameter probe, 0.025 in/min rate; ASTM C165 MOD | |||
| 25 % @Thickness 3.17 mm, Pressure 0.172 MPa | 25 % @Thickness 0.125 in, Pressure 25.0 psi | 0.5" diameter probe, 0.025 in/min rate; ASTM C165 MOD | |||
| 25 % @Thickness 2.54 mm, Pressure 0.0689 MPa | 25 % @Thickness 0.100 in, Pressure 10.0 psi | 0.75" diameter round probe with 0.75" diameter circular sample; Method 2 | |||
| 32 % @Thickness 2.54 mm, Pressure 0.138 MPa | 32 % @Thickness 0.100 in, Pressure 20.0 psi | 0.75" diameter round probe with 0.75" diameter circular sample; Method 2 | |||
| 35 % @Thickness 3.17 mm, Pressure 0.345 MPa | 35 % @Thickness 0.125 in, Pressure 50.0 psi | 0.5" diameter probe, 0.025 in/min rate; ASTM C165 MOD | |||
| 35 % @Thickness 2.54 mm, Pressure 0.0689 MPa | 35 % @Thickness 0.100 in, Pressure 10.0 psi | 1" square probe with 0.5" diameter circular sample; Method 1 | |||
| 40 % @Thickness 2.54 mm, Pressure 0.276 MPa | 40 % @Thickness 0.100 in, Pressure 40.0 psi | 0.75" diameter round probe with 0.75" diameter circular sample; Method 2 | |||
| 42 % @Thickness 2.54 mm, Pressure 0.138 MPa | 42 % @Thickness 0.100 in, Pressure 20.0 psi | 1" square probe with 0.5" diameter circular sample; Method 1 | |||
| 48 % @Thickness 2.54 mm, Pressure 0.276 MPa | 48 % @Thickness 0.100 in, Pressure 40.0 psi | 1" square probe with 0.5" diameter circular sample; Method 1 | |||
| 48 % @Thickness 2.54 mm, Pressure 0.414 MPa | 48 % @Thickness 0.100 in, Pressure 60.0 psi | 0.75" diameter round probe with 0.75" diameter circular sample; Method 2 | |||
| Outgassing - Total Mass Loss | 0.090 % | 0.090 % | CVCM; ASTM E595 | ||
| 0.35 % | 0.35 % | TML; ASTM E595 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore OO | 25 | 25 | ASTM D2240 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 6.5 @Frequency 1.00e+6 Hz | 6.5 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| Dielectric Strength | 7.87 kV/mm | 200 kV/in | |||
| Dissipation Factor | 0.013 @Frequency 1.00e+6 Hz | 0.013 @Frequency 1.00e+6 Hz | Chomerics Test | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 250 µm/m-°C | 139 µin/in-°F | ASTM E831 | ||
| Specific Heat Capacity | 1.00 J/g-°C | 0.239 BTU/lb-°F | ASTM E1269 | ||
| Thermal Conductivity | 1.50 W/m-K | 10.4 BTU-in/hr-ft²-°F | ASTM D5470 | ||
| Maximum Service Temperature, Air | 200 °C | 392 °F | |||
| Minimum Service Temperature, Air | -55.0 °C | -67.0 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 18.0 Month | 18.0 Month | From date of shipment A; Chomerics | ||
| 24.0 Month | 24.0 Month | From date of shipment G; Chomerics | |||
| Descriptive Properties | |||||
| Carrier | G=Fiberglass, A=Aluminum | ||||
| Color | Blue | ||||